{"_buckets": {"deposit": "fdad05fe-491d-42de-8087-345ebc765d90"}, "_deposit": {"created_by": 2, "id": "15659", "owners": [2], "pid": {"revision_id": 0, "type": "depid", "value": "15659"}, "status": "published"}, "_oai": {"id": "oai:nagasaki-u.repo.nii.ac.jp:00015659", "sets": ["19"]}, "author_link": ["58261", "58258", "58257", "58259", "58256", "58260"], "item_2_alternative_title_19": {"attribute_name": "その他のタイトル", "attribute_value_mlt": [{"subitem_alternative_title": "Optical Properties of PbO-GeO_2-R_2O (R=K or Na) Glasses Containing Ni^\u003c2+\u003e Ions : Optical Absorption in the Visible and Infra-Red Region, and Refractive Index"}]}, "item_2_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "1984-11", "bibliographicIssueDateType": "Issued"}, "bibliographicIssueNumber": "1071", "bibliographicPageEnd": "628", "bibliographicPageStart": "622", "bibliographicVolumeNumber": "92", "bibliographic_titles": [{"bibliographic_title": "窯業協會誌"}, {"bibliographic_title": "Journal of the Ceramic Association, Japan", "bibliographic_titleLang": "en"}]}]}, "item_2_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "PbO-GeO2-R2O (R=K or Na)、PbO-GeO2-K2O-Na2Oガラス中のNi2+イオンの吸収スペクトルを測定し、これを用いて配位子場強度、Racahパラメーター及びNi2+イオンの配位状態を決定した。アルカリ含有によるこれらのパラメーターの変化をガラス構造と関連付けて検討した。PbO-GeO2-R2O-NiO(R=K or Na)系ガラスでは、アルカリ含量の増加に伴い配位子場強度を表すピークの位置は高波数側へ、Racahパラメーターは低波数側へシフトした。PbO-GeO2-K2O-Na2O-GeO2マトリックスガラス中では、Ni2+は6配位が支配的であるが、アルカリ含量増加に伴い4配位と6配位のNi2+が生成する。これらの測定結果から、この系のガラス中にはGeO8-6イオンが生成していることが示唆された。PbO-GeO2-R2O-NiO(R=K or Na), PbO-GeO2-K2O-Na2O-NiO系ガラスのIR吸収スペクトルを測定し、これを用いてGeの配位状態を決定した。結果として、この系のガラス中ではGeは6配位が支配的であり、アルカリの添加によってGeの配位数はあまり大きい変化を受けないことが示された。PbO-GeO2-R2O-NiO(R=K or Na), PbO-GeO2-K2O-Na2O系ガラスの屈折率を測定した。PbO-GeO2-R2O-NiO系ガラスではアルカリ含有増加に伴い屈折率は低下し、加成性からのわずかなずれが見られた。PbO-GeO2-K2O-Na2O-NiO系ガラスでは、[K2O]/[K2O+Na2O]の比の増加に伴い屈折率は直線的に低下し、混合アルカリ効果ははっきりとは現れなかった。", "subitem_description_type": "Abstract"}, {"subitem_description": "Absorption spectra of Ni2+ ions in PbO-GeO2-R2O (R=K or Na) and PbO-GeO2-K2O-Na2O glasses were measured. The ligand field strength and the Racah parameter were calculated from the absorption wave numbers. The state of coordination of Ni2+ ions was elucidated from the peak positions. With increasing alkali content in PbO-GeO2-R2O-NiO(R=K or Na) glasses, the peak wave number corresponding to the ligand field strength increased and the Racah parameter decreased. In PbO-GeO2-K2O-Na2O-NiO glasses, the ligand field strength and the Racah parameter wave not calculated. Ni2+ ions were considered to be predominantly in the 6 coordination state in PbO-GeO2 glasses. The increase in alkali content in PbO-GeO2-R2O (R=K or Na) glass resulted in the tetragonal and tetrahedral structures. The result obtained suggests that GeO8-6 ions are formed by adding alkali ions to the glass network.", "subitem_description_type": "Abstract"}]}, "item_2_description_63": {"attribute_name": "引用", "attribute_value_mlt": [{"subitem_description": "窯業協会誌, 92(1071), pp.622-628; 1984", "subitem_description_type": "Other"}]}, "item_2_full_name_3": {"attribute_name": "著者別名", "attribute_value_mlt": [{"nameIdentifiers": [{"nameIdentifier": "58259", "nameIdentifierScheme": "WEKO"}], "names": [{"name": "Oyamada, Ryozo"}]}, {"nameIdentifiers": [{"nameIdentifier": "58260", "nameIdentifierScheme": "WEKO"}], "names": [{"name": "Koga, Hideto"}]}, {"nameIdentifiers": [{"nameIdentifier": "58261", "nameIdentifierScheme": "WEKO"}], "names": [{"name": "Shimomichi, Tsuyoshi"}]}]}, "item_2_publisher_33": {"attribute_name": "出版者", "attribute_value_mlt": [{"subitem_publisher": "日本セラミックス協会"}]}, "item_2_relation_42": {"attribute_name": "関係URI", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "http://ci.nii.ac.jp/naid/110002313312/"}]}]}, "item_2_rights_13": {"attribute_name": "権利", "attribute_value_mlt": [{"subitem_rights": "社団法人日本セラミックス協会"}, {"subitem_rights": "本文データは学協会の許諾に基づきCiNiiから複製したものである"}]}, "item_2_source_id_10": {"attribute_name": "書誌レコードID", "attribute_value_mlt": [{"subitem_source_identifier": "AN00245658", "subitem_source_identifier_type": "NCID"}]}, "item_2_source_id_7": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "00090255", "subitem_source_identifier_type": "ISSN"}]}, "item_2_text_62": {"attribute_name": "出版者別言語", "attribute_value_mlt": [{"subitem_text_value": "The Ceramic Society of Japan"}]}, "item_2_version_type_16": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "小山田, 了三"}], "nameIdentifiers": [{"nameIdentifier": "58256", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "古賀, 秀人"}], "nameIdentifiers": [{"nameIdentifier": "58257", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "下道, 毅"}], "nameIdentifiers": [{"nameIdentifier": "58258", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2020-12-23"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "110002313312.pdf", "filesize": [{"value": "536.4 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_free", "mimetype": "application/pdf", "size": 536400.0, "url": {"label": "110002313312.pdf", "url": "https://nagasaki-u.repo.nii.ac.jp/record/15659/files/110002313312.pdf"}, "version_id": "86b7a062-076b-41b3-8ed7-466d7f5967f7"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "PbO-GeO_2-R_2O-NiO glasses", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Mixed alkali effect", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Optical property (visble, IR, refractive index)", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Glass structure", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Ligand field of Ni^\u003c2+\u003e ion", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "journal article", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "Ni^\u003c2+\u003eイオン含有PbO-GeO_2-R_2O(R=K or Na)系ガラスの光学的性質 : 可視域, 赤外域の光吸収及び屈折率", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "Ni^\u003c2+\u003eイオン含有PbO-GeO_2-R_2O(R=K or Na)系ガラスの光学的性質 : 可視域, 赤外域の光吸収及び屈折率"}]}, "item_type_id": "2", "owner": "2", "path": ["19"], "permalink_uri": "http://hdl.handle.net/10069/23589", "pubdate": {"attribute_name": "公開日", "attribute_value": "2010-08-20"}, "publish_date": "2010-08-20", "publish_status": "0", "recid": "15659", "relation": {}, "relation_version_is_last": true, "title": ["Ni^\u003c2+\u003eイオン含有PbO-GeO_2-R_2O(R=K or Na)系ガラスの光学的性質 : 可視域, 赤外域の光吸収及び屈折率"], "weko_shared_id": 2}
Ni^<2+>イオン含有PbO-GeO_2-R_2O(R=K or Na)系ガラスの光学的性質 : 可視域, 赤外域の光吸収及び屈折率
http://hdl.handle.net/10069/23589
http://hdl.handle.net/10069/23589f5c80c2d-a03b-45cb-8699-30d2e6b51592
名前 / ファイル | ライセンス | アクション |
---|---|---|
110002313312.pdf (536.4 kB)
|
|
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2010-08-20 | |||||
タイトル | ||||||
タイトル | Ni^<2+>イオン含有PbO-GeO_2-R_2O(R=K or Na)系ガラスの光学的性質 : 可視域, 赤外域の光吸収及び屈折率 | |||||
言語 | ||||||
言語 | jpn | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | PbO-GeO_2-R_2O-NiO glasses | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Mixed alkali effect | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Optical property (visble, IR, refractive index) | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Glass structure | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Ligand field of Ni^<2+> ion | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
資源タイプ | journal article | |||||
著者 |
小山田, 了三
× 小山田, 了三× 古賀, 秀人× 下道, 毅 |
|||||
著者別名 | ||||||
姓名 | Oyamada, Ryozo | |||||
著者別名 | ||||||
姓名 | Koga, Hideto | |||||
著者別名 | ||||||
姓名 | Shimomichi, Tsuyoshi | |||||
その他のタイトル | ||||||
その他のタイトル | Optical Properties of PbO-GeO_2-R_2O (R=K or Na) Glasses Containing Ni^<2+> Ions : Optical Absorption in the Visible and Infra-Red Region, and Refractive Index | |||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | PbO-GeO2-R2O (R=K or Na)、PbO-GeO2-K2O-Na2Oガラス中のNi2+イオンの吸収スペクトルを測定し、これを用いて配位子場強度、Racahパラメーター及びNi2+イオンの配位状態を決定した。アルカリ含有によるこれらのパラメーターの変化をガラス構造と関連付けて検討した。PbO-GeO2-R2O-NiO(R=K or Na)系ガラスでは、アルカリ含量の増加に伴い配位子場強度を表すピークの位置は高波数側へ、Racahパラメーターは低波数側へシフトした。PbO-GeO2-K2O-Na2O-GeO2マトリックスガラス中では、Ni2+は6配位が支配的であるが、アルカリ含量増加に伴い4配位と6配位のNi2+が生成する。これらの測定結果から、この系のガラス中にはGeO8-6イオンが生成していることが示唆された。PbO-GeO2-R2O-NiO(R=K or Na), PbO-GeO2-K2O-Na2O-NiO系ガラスのIR吸収スペクトルを測定し、これを用いてGeの配位状態を決定した。結果として、この系のガラス中ではGeは6配位が支配的であり、アルカリの添加によってGeの配位数はあまり大きい変化を受けないことが示された。PbO-GeO2-R2O-NiO(R=K or Na), PbO-GeO2-K2O-Na2O系ガラスの屈折率を測定した。PbO-GeO2-R2O-NiO系ガラスではアルカリ含有増加に伴い屈折率は低下し、加成性からのわずかなずれが見られた。PbO-GeO2-K2O-Na2O-NiO系ガラスでは、[K2O]/[K2O+Na2O]の比の増加に伴い屈折率は直線的に低下し、混合アルカリ効果ははっきりとは現れなかった。 | |||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | Absorption spectra of Ni2+ ions in PbO-GeO2-R2O (R=K or Na) and PbO-GeO2-K2O-Na2O glasses were measured. The ligand field strength and the Racah parameter were calculated from the absorption wave numbers. The state of coordination of Ni2+ ions was elucidated from the peak positions. With increasing alkali content in PbO-GeO2-R2O-NiO(R=K or Na) glasses, the peak wave number corresponding to the ligand field strength increased and the Racah parameter decreased. In PbO-GeO2-K2O-Na2O-NiO glasses, the ligand field strength and the Racah parameter wave not calculated. Ni2+ ions were considered to be predominantly in the 6 coordination state in PbO-GeO2 glasses. The increase in alkali content in PbO-GeO2-R2O (R=K or Na) glass resulted in the tetragonal and tetrahedral structures. The result obtained suggests that GeO8-6 ions are formed by adding alkali ions to the glass network. | |||||
書誌情報 |
窯業協會誌 en : Journal of the Ceramic Association, Japan 巻 92, 号 1071, p. 622-628, 発行日 1984-11 |
|||||
出版者 | ||||||
出版者 | 日本セラミックス協会 | |||||
出版者別言語 | ||||||
The Ceramic Society of Japan | ||||||
ISSN | ||||||
収録物識別子タイプ | ISSN | |||||
収録物識別子 | 00090255 | |||||
書誌レコードID | ||||||
収録物識別子タイプ | NCID | |||||
収録物識別子 | AN00245658 | |||||
権利 | ||||||
権利情報 | 社団法人日本セラミックス協会 | |||||
権利 | ||||||
権利情報 | 本文データは学協会の許諾に基づきCiNiiから複製したものである | |||||
著者版フラグ | ||||||
出版タイプ | VoR | |||||
出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
関係URI | ||||||
関連名称 | http://ci.nii.ac.jp/naid/110002313312/ | |||||
引用 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 窯業協会誌, 92(1071), pp.622-628; 1984 |